Polymerised CNSL is specially used in Brake Lining Industry
Specification
SG-325
| Viscosity at 30°C | 27000-37000cps |
|
Polymerization Time (Hot Plate Method) |
25-45 sec |
| PH value | 3-4 |
SG-215
| Viscosity at 30°C | 260-270cps |
|
Polymerization Time (Hot Plate Method) |
2-4 min |
| PH value | 8.5-9.5 |
| Volatile loss | <2% |
SG-205
| Viscosity at 30°C | 50,000cps |
| Polymerization Time | 3-4 minutes |
| Ash Content | 2% |
| Gel time @ 121°C (8% Hexa) | 6-7 minutes |
| PH Water Extract | Colourless |
AX-225
|
Viscosity at 25°C (Brooke Field, Spindle-4, RPM-12) |
25,000cps-28,000cps |
| Polymerization Time – Hot Plate at 150°C | 4 min max |
| Acid Value | <3 |
| Ash Content | <2% |
| PH value | 6-8 |
AX-220
|
Viscosity at 25°C (Brooke Field, Spindle-4, RPM-12) |
14,500cps |
|
Polymerization Time |
3-4 minutes |
|
Acid Value |
<3 |
|
Ash Content |
<2% |
|
PH value |
6-8 |
|
Aqua solution 10% filtration colour |
Clear |